镍钛矫正弓丝的弯制与加热定形

来源:网络 时间:2012/6/13

提 要 目的 提出一种弯制镍钛丝的方法,以期对这种高弹性形状记忆钢丝重新定形、加弯制司匹氏曲度及多种微小弯曲。方法 利用点焊-加热三用机的加热装置配合热处理钳等,对镍钛丝进行通电加热,从而达到弯制后定形的目的。结论 当给镍钛丝加上比Af点高60℃以上的温度时,则相变引起的形状恢复应力超过丝材本身的屈服应力,合金形状记忆特性被部分影响。利用该方法可再次确定镍钛丝的形状,对提高矫治疗效极其有利。

Bending and Heat-molding of Ni-Ti Orthodontic Wires

Yao Sen, et al.

Center of Orthodontics, 174 Hospital of PLA, Xiamen 361003,

Abstract objective Aim of this paper is to introduce a bending method for Ni-Ti orthodontic wire, in roder to remold, put Spee’s curves and other micro-bends to this super-elasticity and shape memory alloy wire.Method To electrify-heat the Ni-Ti wire. with a Heat Treat Device and two Pliers which connected to the Device, in order to bend and remold the Ni-Ti wire.Conclusion When the Ni-Ti wire was heated over 60℃ than point Af, the shape recovery stress caused by the transformation is larger than the bend stress of alloy wire itself, and shape memory characteristic of the alloy was affected partly, so the Ni-Ti wire shape can be changed by the method, this will be useful to satisfying orthodontic results.

Key words Ni-Ti wrieBend Heattreatment

材料与方法

仪器与材料

仪器:西安天隆新技术研究所研制的FS-4000齿科点焊-加热三用机(包括加热装置及热处理钳)。

镍钛丝:北京有色金属研究总院生产的预成弓型镍钛丝(批号:970305):

圆丝:.016”;方丝:.018”×.025”。

镍钛丝的弯制

1. 镍钛丝弓型的重新调节

镍钛矫正弓丝在出厂时已被制作成了一定的弓型,其宽度不一定与每个患者的牙弓宽度相匹配,不利于矫治的进行,应该对镍钛丝的弓型宽度重新进行调节〔1、2〕。具体的方法是:将预成弓型的镍钛丝夹在点焊加热三用机的加热板上,调节镍钛丝的宽度与患者牙弓宽度相匹配。将点焊-加热三用机的功率调节至最大,点按加热开关,给镍钛丝加热,使镍钛丝瞬间即将变红(但尚未变红)(温度约为360℃〔3〕)。镍钛丝弓型调节即可完成。

2. 镍钛丝司匹氏曲的弯制

在使用镍钛丝打开咬、压低前牙时,往往需要给弓丝加弯司匹氏曲,才能起到良好的效果。具体的方法是:将预成弓型镍钛丝夹在点焊-加热三用机的加热板上并调节弓丝的宽度与患者牙弓宽度相匹配。左手持细玻璃棒于弓丝的中点处上挑弓丝,加弯司匹氏曲度(图1),右手点按加热开关,给弓丝通电加热,使弓丝瞬间即将变红(但尚未变红)。取下已有司匹氏曲度的弓丝。将镍钛丝热处理钳及脚控开关装配在点焊-加热三用机上,调节功率旋钮至合适的位置(一般为刻度的4.5),利用热处理钳将镍钛丝的末端内收,通电加热,即可将预成弓型的镍钛丝调节成与患者牙弓宽度相匹配的带司匹氏曲度的弓丝(图2)。

图1 给镍钛丝加弯司匹氏曲

图2 将镍钛丝末段内收,将左边的形状改为右边的形状

3. 镍钛丝微小弯曲的弯制

微小弯曲指的是在磨牙颊侧管前给镍钛弓丝弯制必要的磨牙外展弯、后倾曲、末端内收弯。